Abstract
Thermoluminescence (TL) dosimetry was used to measure dose effects on the raw stock material of borosilicate container glass from different geographical locations. Effects were studied at times up to 60 days post-irradiation at doses from 0.15 to 20 Gy. The minimum detectable dose using this technique was estimated to be 0.15 Gy which is roughly equivalent to a 24 hr irradiation 1 cm from a 50 ng source of 60Co. Two peaks were identified in the TL glow curve, a relatively unstable peak around 125°C and a more stable peak around 225°C. Differences in TL glow curve shape and intensity were also observed for the glasses from different geographical origins. We investigate radiation induced defects in glass to further develop the technique of intrinsic dosimetry±the measurement of the total absorbed dose received by the walls of a container holding radioactive material. Intrinsic dosimetry is intended to be used as an interrogation tool to provide enhanced pathway information on interdicted or newly discovered waste containers of unknown origin or history by considering the total absorbed dose received by a container in tandem with the physical characteristics of the radioactive material housed within that container. One hypothetical scenario is presented to illustrate the application of intrinsic dosimetry to waste management and nuclear forensics.